SURFACING
AND HARDFACING
G. HIGH TEMPERATURE AND CORROSION WEAR RESISTANT ALLOYS |
UTP PRODUCT | HARDNESS | APPLICATION FIELD |
MMA
|
MIG
|
F/C
WIRE
|
TIG
|
7000
|
APPROX.
200HB
Work hardening to 450HB |
Rutile
based coated electrode
180% metal recovery Wear resistant cladding on parts subject to high heat, thermal shock and scaling. |
||||
7010
|
APPROX.
200HB
Work hardening to 450HB |
Basic coated
electrode For parts subject to high heat thermal shock, compression, impact and abrasion Heat resistant up to 700°C |
COBALT
BASED ALLOYS
|
CELSIT
721 |
APPROX.: 30-32 HRC After work hard 45HRC At 600°C 240HB |
Rutile
coated electrode.
Crack resistant hardfacing on parts subject to a combination of all types of wear. Corrosion resistant Working temperature up to 900°C |
|
|
||
CELSIT
706
A. CELSIT 706 AF. CELSIT 706 |
APPROX.: 40-42 HRC Hardness at 600°C 240HB |
Rutile
coated electrode.
High grade hardfacing on parts subject to a combination of all types of wear Corrosion resistant Working temperature up to 900°C |
|
|
||
CELSIT
V
|
As above |
Basic
coated electrode (same as CELSIT 706)
|
||||
A.
CELSIT F
|
APPROX.: 45-48 HRC Hardness at 600°C 300HB |
A Co
Cr Ni W - Alloyed wire for TIG and Oxyacetylene welding.
High grade hardfacing Corrosion resistant Working temperature up to 900°C |
||||
CELSIT
712
A. CELSIT 712SN AF. CELSIT 712 |
APPROX.: 48-50 HRC Hardness at 600°C 40 HRC |
Rutile
coated electrode. High wear resistance on parts subject to a combination of all types of wear. Corrosion resistant Working temperature up to 900°C |
|
|
||
CELSIT
SN
|
As above | Basic coated electrode (same as CELSIT 712) | ||||
CELSIT
701
A. CELSIT 701N AF. CELSIT 701 |
APPROX.: 54-56 HRC At 600°C 42HRC At 800°C 34HRC |
Rutile
coated electrode. Highly wearing parts subject to severe abrasion in a combination with corrosion at high temperature Working temperature up to 900°C |
|
|