SURFACING AND HARDFACING
F. HOT AND COLD WORKING STEELS. WEAR RESISTANT ALLOYS

BACK TO SURFACING AND HARDFACING PRODUCT RANGE

UTP PRODUCT HARDNESS APPLICATION FIELD
MMA
MIG
TIG
F/C WIRE
73 G2

A73 G2
APPROX: 55 HRC
Basic coated electrode
Surfacing hot and cold working steels subject to severe friction, compression and moderate impact. Heat resistant up to 550°C.







73 G3

A73 G3
APPROX:
45 - 50 HRC 		Basic coated electrode
Surfacing hot working steels exposed to impact, compression and abrasion. Heat resistant up to 550°C.







73 G4

A73 G4
APPROX:
38 - 42 HRC 		Basic coated electrode
Surfacing hot working steels for tough resistance against impact, compression and abrasion. Heat resistant up to 550°C.







673
APPROX: 58 HRC Rutile coated electrode
Surfacing and repairing hot and cold working tools. High wear resistant against abrasion and compression. Ideal for edge build ups. Heat resistant up to 550°C.
690
 APPROX: 62 HRC Rutile coated electrode
150% metal recovery
Surfacing of cutting tools subject to friction, compression and impact. Deposit equivalent to high speed steel. Heat treatable. Heat resistant up to 550°C.
A696
 60-64 HRC For the repair of high speed steels and cutting tools of non-alloy and low-alloy materials.
694
 APPROX:
50 - 52 HRC 		Basic coated electrode
120% metal recovery
Surfacing of hot working steels. Resistant to friction and compression. Temperature resistant up to 550°C.
702

A702
 APPROX.: Untreated
34 - 37 HRC
Age hardening
3-4h/480°C
50 - 54HRC 		Basic coated electrode
Age-hardenable
High wear resistant on tools
Ideal for highly stressed hot and cold tooling.







750

APPROX:
48 - 52 HRC

Rutile coated electrode
Ideally suited for surfacing on hot working tools up to 650°C.
Excellent where metallic sliding wear and high change in temperature stress is present

BACK TO SURFACING AND HARDFACING PRODUCT RANGE