SURFACING
AND HARDFACING
E. EXTREME ABRASION WEAR RESISTANT ALLOYS |
UTP PRODUCT | HARDNESS | APPLICATION FIELD |
MMA
|
TIG
|
F/C
WIRE
|
LEDURIT
65
|
APPROX: 65 HRC |
BASIC
coated high efficiency electrode
240% metal recovery High resistant to extreme abrasion up to 500°C due to inclusion of Mo.V.W.Nb. Working parts in cement and brick industry |
|||
AF.LEDURIT
68
|
APPROX: 63 - 65 HRC |
Flux cored
Niobium carbide wire. Extreme abrasion. Working temperature up to 450°C. Ideal for parts exposed to wear by dust, sand, gravel, cement etc. |
|||
AF.LEDURIT
70
|
APPROX: 68 HRC | Flux cored
Chromium carbide wire. Extreme abrasion. Working temperature up to 600°C. Ideal for sinter crushers, fire grate bars, blast furnace bells and chutes. |
|||
75
|
APPROX:
65 HRC Micro hardness of Tungsten carbides 2500 HV |
Basic coated
electrode with sintered core wire on tungsten carbide base. Extremely severe mineral abrasion, sand etc. Ideal for screw conveyors, mixers and blades. |
|||
AF.LEDURIT
76
|
APPROX: 68 HRC | Flux cored
Chromium carbide wire. Extremely high abrasion. Working temperature up to 700°C. |